MG765 1/8 ELECTRODE 10LB TUBE SEVERE ABRASION, MILD IMPACT
Item Code: MESMG76532
SEVERE ABRASION, MILD IMPACT
GENERAL CHARACTERISTICS:
MG 765 is designed for use on carbon and low alloy steels, manganese steels and cast iron. Deposits take a
high polish, which contributes to high friction and abrasion wear resistance, especially against small particle
abrasion. Excellent on applications that need impact as well as abrasion resistance. Deposits well out of position.
APPLICATIONS:
MG 765 is recommended for severe abrasion applications, along with moderate impact. This alloy also has
good hot hardness up to approximately 1000°F. Especially designed for crusher applications. Used heavily in
construction, mining, brick and clay industries on parts such as crusher rolls, jaw crushers, bucket teeth,
edges, hammers, mill hammers, conveyor screws, etc.
TECHNICAL DATA:
Hardness As welded: up to 57-61 HRC
Polarity: AC or DC reverse (electrode +)
Diameter / Amperage:
3/32” (2.4mm) 75-110
1/8” (3.2mm) 90-130
5/32” (4.0mm) 120-170
3/16” (5.0mm) 140-200
1/4” (6.4mm) 200-250
PROCEDURE:
Remove any fatigued or unsound metal with MG 570. According to the thickness of deposit and type of base
metal, a padding of MG 740, MG 750, or MG 600 might be considered. On cast iron, a base of MG 200 is
recommended. Deposits can be applied as stringer beads; however, weave passes are recommended for
maximum deposition rate. Prevent excessive heat build-up. Allow parts to cool slowly.
Category
Stick Electrode
Description
SEVERE ABRASION, MILD IMPACT
GENERAL CHARACTERISTICS:
MG 765 is designed for use on carbon and low alloy steels, manganese steels and cast iron. Deposits take a
high polish, which contributes to high friction and abrasion wear resistance, especially against small particle
abrasion. Excellent on applications that need impact as well as abrasion resistance. Deposits well out of position.
APPLICATIONS:
MG 765 is recommended for severe abrasion applications, along with moderate impact. This alloy also has
good hot hardness up to approximately 1000°F. Especially designed for crusher applications. Used heavily in
construction, mining, brick and clay industries on parts such as crusher rolls, jaw crushers, bucket teeth,
edges, hammers, mill hammers, conveyor screws, etc.
TECHNICAL DATA:
Hardness As welded: up to 57-61 HRC
Polarity: AC or DC reverse (electrode +)
Diameter / Amperage:
3/32” (2.4mm) 75-110
1/8” (3.2mm) 90-130
5/32” (4.0mm) 120-170
3/16” (5.0mm) 140-200
1/4” (6.4mm) 200-250
PROCEDURE:
Remove any fatigued or unsound metal with MG 570. According to the thickness of deposit and type of base
metal, a padding of MG 740, MG 750, or MG 600 might be considered. On cast iron, a base of MG 200 is
recommended. Deposits can be applied as stringer beads; however, weave passes are recommended for
maximum deposition rate. Prevent excessive heat build-up. Allow parts to cool slowly.